What causes stainless steel tank deformation

Stainless steel water tank is a common water storage tool in daily life, stainless steel water tank can be applied in different fields, can be in daily life, fire water, hotel restaurants, hospitals and large shopping malls and other venues, different stainless steel raw materials make the service life of stainless steel water tank and the actual effect will not be the same, Next, Jiansheng stainless steel and you will say what causes the deformation of stainless steel tank.

1, stainless steel water tank punching plate material when unloading method is wrong, in the staff unloading, some workers for convenience, the selection of steel wire rope and chain will be the whole stainless steel water tank punching plate unloading together, such operation will cause at the bottom of the punching plate because of the lifting surface is small, under too much pressure, It is very likely that there will be deformation of the edge of the punching plate. So when unloading the staff need to carry out safety awareness and corresponding training guidance, and arrange full-time personnel to supervise the process of unloading, to ensure that the stainless steel punching plate will not be deformed when unloading, to avoid deformation when installing stainless steel water tank.

2, stainless steel water tank pressing plate stacking unreasonable plate deformation will also occur. Plate in the transportation to the installation site due to stacking time comparison factory, and did not do a good job of site stacking environment finishing and protection, in order to save space, the different sizes and thickness of stainless steel stamping plate are stacked together, stacked punching plate after the number of plate is too much, it will be easy to appear plate deformation, which will affect the finished stainless steel water tank quality and aesthetic degree. So when stacking plates need to use some protective items, all stainless steel punching plate in accordance with the size and specifications of the classification placed, reduce the opportunity of plate deformation.

3, stainless steel water tank punching plate before installation did not do calibration work, some plate before installation defects and deformation, in the installation of stainless steel water tank before the need to calibrate the plate. But if the plate meets the installation requirements, after welding, after removing the anti-deformation tool, under the action of internal stress, it will still cause the stamping plate deformation is serious, and then cause the deformation of the stainless steel water tank. This requires the installation personnel before installation, to detect the quality of the stamped plate, found that there is a deformation condition to timely calibration, stainless steel water tank is reasonably installed, to prevent deformation and other problems.

4, in the calibration process of the installation of stainless steel water tank, in the use of sledgehammer calibration is not right, with a sledgehammer hammer on the surface of the plate, resulting in an increase in plate surface pits, plate surface coating is damaged, harm the quality of stainless steel plate appearance, such wrong operation will also lead to stainless steel tank deformation. In this case, the construction personnel are required to choose the pad when carrying out sledgehammer calibration, and the tilt of the pad is the same as that of the plate, so as to achieve a good calibration effect.

5, stainless steel tank welding when using too much electricity flow will also lead to stainless steel tank deformation. Some construction personnel in order to project progress, choose to use larger welding flow, welding temperature is higher, stainless steel water tank surface heating area is very large, it is very easy to deformation. This requires the construction personnel must strictly abide by the operating guidelines for the actual operation, not in order to catch up with the progress thus affecting the quality of the stainless steel tank.